Silicon40 Transparent
Click image to view full sizeItem-Name:
Silicon40 Transparent
More-Details:
Technical data
| Compound | A - SA 40 - 79 | - |
|---|---|---|
| Colour | Transparent | |
| Polymer | Silicone | |
| Hardness | 40 +/-5 Shore A | DIN 53 505 |
| Thickness tolerance | +/-0,40 mm |
| Density/Spec. weight | 1,13 +/-0,02 g/cm3 | DIN 53 508 |
|---|---|---|
| Tear strenght | 6,5 N/mm2 | DIN 53 504 |
| Elogation at tear | 600 % | DIN 53 504 |
| Resilience | 25 % | DIN 53 512 |
| Max. temperature | 200 °C | DIN 53 508 |
More Products
Silicon35 White
Technical data Compound A - SA 35 - 80 - Colour White Polymer Silicone Hardness 35 +/-5 Shore A DIN 53 505 Thickness tolerance +/-0,40 mm Density/Spec. weight 1,12 +/-0,02 g/cm3 DIN 53 508 Tear strenght 5,8 N/mm2 DIN 53 504 Elongation at tear 750 % DIN 53 504 Resilience 33 % DIN 53 512 Tensile strenght 8,0 Mpa DIN 53 504 Max. temperature 220 °C DIN 53 508
Silicon Classic
Technical data Compound A - SA 55 - 82 - Colour Grey Material Silicon Hardness 58 Shore A +/-5 DIN 53 505 Thickness tolerance +/-0,4 mm Density/Spec. weight 1,18 g/cm3 DIN 53 508 tensile strenght 9,3 Mpa DIN 53 504 Elongation at tear 600 % DIN 53 504 Resilience 36 % DIN 53 512 Max. temperature 220 °C DIN 53 508
Lamibran
Technical data Backing material Covering layer Composite material Material Silicon Special layer Lamibran® Hardness 55 Shore A 84,8 IRHD - density/Spe. weight 1,17g/qm3 1,17g/qm3 - Tear strenght 8,2 N/mm2 14,9 N/mm2 6,1 N/mm2 Elongation at tear 691% 253% 200%(max.) Resilience 40% - 18% Tear growth resistance (ASTM 624B) 57,0 N/mm2 - 47.0 N/mm2 Module 100% 1,7 N/mm2 2,0 N/mm2 2,8 N/mm2 Module 200% 2,1 N/mm2 - 4,4 N/mm2 Module 300% 2,7 N/mm2 - 5,9 N/mm2 Max. temperature - - 200°C
Soalrbran
Technical Data Width 2700 mm Thickness 3 mm (+/- 0,4 mm) Colour black, smooth/textured Durometer 55 Shore A +/- 5 DIN 53 505 Specific weight 1,07 g/cm² DIN EN ISO 1183-1 Tensile strength 12 N/mm² DIN 53 504 Elongation at tear > 400 % DIN 53 504 Rebound elasticity >= 45% DIN 53 512 Module 100% 1,0 N/mm² DIN 53 504 Module 200% 3,0 N/mm² DIN 53 504 Module 300% 5,8 N/mm² DIN 53 504 Tear resistance 11,4 N/mm DIN ISO 34-1 Temperature range max. 170°C
Silicon55 Grey- XL
Technical data Compund A - SA 55 - 82 - Colour Grey Polymer Silicone Hardness 55 +/-5 Shore A DIN 53 505 Thickness tolerance +/-0,40 mm Density/Spec. weight 1,18 +/-0,02 g/cm3 DIN 53 508 Tear strenght 8,4 N/mm2 DIN 53 504 Elongation at tear 600 % DIN 53 504 Resilience 36 % DIN 53 512 Tensile strenght 9,3 Mpa DIN 53 504 Max. temperature 220 °C DIN 53 508
Silicon55 Grey
Technical data Compund A - SA 55 - 82 - Colour Grey Polymer Silicone Hardness 55 +/-5 Shore A DIN 53 505 Thickness tolerance +/-0,40 mm Density/Spec. weight 1,18 +/-0,02 g/cm3 DIN 53 508 Tear strenght 8,4 N/mm2 DIN 53 504 Elongation at tear 600 % DIN 53 504 Resilience 36 % DIN 53 512 Tensile strenght 9,3 Mpa DIN 53 504 Max. temperature 220 °C DIN 53 508